Irregular TC4 Powder Hydrogenation Dehydrogenation (TC4) Shaping TC4 Titanium Alloy Powder
Our Ti-6AI-4V titanium powder is produced using a proprietary hydrogenation/dehydrogenation (HDH) process, offering a variety of particle size distribution options. This production process is both sustainable and scalable, making it a cost-effective alternative to other titanium powder production technologies.
Particle size: 15-53um, 0-25um, 15-45um, 53-150um, customized
Product appearance: gray powder;
Product features: 1. Low oxygen content, low price, certain fluidity, can replace traditional spherical shapes
2. The powder has high purity, and the particle size and residual chemical indicators are strictly controlled.
3. The Ti-6A1-4V powder produced using HDH has particles without pores.
Application areas: Our hydrogenated dehydrogenation TC4 powder is widely used in additive manufacturing, medical equipment, 3C, metal injection molding, powder metallurgy, sputtering targets, industrial applications, and 3D printing
Characteristic
1. High purity, particle size, and residual chemical indicators are strictly controlled.
2. Ti-6AI-4V powder produced using HDH has particles without pores.
3. These powders meet the chemical requirements of medical ASTM F1580.
Specification parameters
典型产品
Typical Produc |
氢化脱氢TC4粉 HDH Ti-6Al-4V Powder |
规格μm
Specifications |
0-25 |
0-45 |
15-53 |
20-60 |
20-75 |
粒度分布/μm
Particle Size
Distribution |
D10 |
4-7 |
11-17 |
14-19 |
18-23 |
20-25 |
| D50 |
12-15 |
27-32 |
32-37 |
36-42 |
41-47 |
| D90 |
22-27 |
41-48 |
50-56 |
57-64 |
68-75 |
松装密度/(g/cm³)
Apparent Densityl(g/cm³) |
1.0-1.2 |
1.1-1.3 |
1.3-1.5 |
1.35-1.6 |
1.4-1.7 |
振实密度/(g/cm³)
Tap Dansityllg/cm³) |
1.8-2.0 |
1.9-2.1 |
2.1-2.3 |
2.1-2.3 |
2.1-2.3 |
氧含量/(ppm)
Oxygen Content/(ppm) |
≤0.30 |
≤0.25 |
≤0.18 |
≤0.16 |
≤0.16 |
制备工艺
Preparation Method |
HDH |
化学成分(wt.%)
ChemicalComponent |
Al:5.50-6.75; V:3.50-4.50; Fe:≤0.2; N:≤0.015;
C:≤0.015; Cl:≤0.03; H:≤0.02; O:/; Ti:Bal |
Product Quality Inspection Report
Product Tags:
|
|
Irregular TC4 Titanium Alloy Powder Hydrogenation Dehydrogenation Ti6Al4V Powder Images
|